Seeing below the surface of bimetallic nanoparticles

Journal Reference:

  1. Nobutomo Nakamura, Koji Matsuura, Akio Ishii, Hirotsugu Ogi. Restructuring in bimetallic core-shell nanoparticles: Real-time observation. Physical Review B, 2022; 105 (12) DOI: 10.1103/PhysRevB.105.125401

Core-shell nanoparticles comprise one type of material encapsulated within another and offer properties that are not available using just one material.

When the materials are metals, and one is deposited on top of the other, certain features of the metals — for example the atom size and the surface energy — mean they should organize with a particular metal as the shell. However, in practice, the result is not always what is expected and can change depending on the experimental procedure.

Methods for analyzing core-shell nanomaterials are generally applied after synthesis, providing little insight into what is happening during the formation process. The researchers therefore developed a technique that allowed them to follow the metal deposition and restructuring in real time at room temperature.

“Our technique is based on the idea that if the higher surface energy metal forms the shell, the surface area of the particle wants to minimize so it tightens the sphere,” explains first author Nobutomo Nakamura. “However, if there is interdiffusion of the metals, the structure of the core-shell particles is more dispersed. We therefore tracked the difference in particle shape using a piezoelectric resonator.”

The shape changes were followed by growing nanoparticles very close together on a substrate and then monitoring the interparticle distance through the resistance.

If the electric field excited by the resonator caused electrons to move between particles that were spaced apart, then the resistance was high because the flow was interrupted by the gaps. However, if the particles spread and touched, forming a continuous path, then the resistance decreased. This information was then used to interpret what was happening inside the particles.

The system was used to investigate three different combinations of two metals, deposited in both orders. It was found that the depositions could be followed in real time and deposition of gold followed by palladium notably led to interdiffusion, forming core-shell particles with a structure opposite to the deposition order.

“Our technique offers the opportunity to fine-tune the preparation of bimetallic core-shell nanoparticles,” says Associate Professor Nakamura. “This control is expected to lead to the custom design of nanomaterials for applications such as hydrogen sensing and sustainable processing.”

We would love to say thanks to the writer of this write-up for this remarkable material